Zirconia Fused Alumina 25

Zirconia fused alumina 25 is made of high-purity alumina and fused zirconia as raw materials. It is smelted at a high temperature of 2250 ° C and formed by special processing technology and Barmac ball milling. It is of high quality, extremely hard, compact in structure and special crystal. Branched eutectic structure. Zirconium fused alumina can be divided into ZA25 zirconia fused alumina (ZrO2 25%) and ZA40 zirconia fused alumina (ZrO2 40%) according to the content of ZrO2.

Description of Zirconia Fused Alumina 25

Grade

Al2O3(%)

ZrO2 (%)

TiO2(%)

Fe2O3(%)

SiO2(%)

ZA25

68-72

24-30

≤1.5

≤0.5

≤1.0

ZA40

55-57

35-44

≤1.5

≤0.5

≤1.0

Available Sizes

0-0.5MM 0.5-1MM 1-1.5MM 1.5-2MM 2.5-3MM 3-3.5MM 3.5-4MM 0-1MM 1-2MM 2-3MM 1-3MM 3-5MM 4-5MM 3-6MM 5-8MM

F4 F8 F10 F12 F14 F16 F20 F22 F24 F30 F36 F46 F54 F60 F70 F80 F90 F100 F120 F150 F180 F220

JIS#4 JIS#5 JIS#6 JIS#7 JIS#8 JIS#10 JIS#12 JIS#14 JIS#16 JIS#20 JIS#24 JIS#30 JIS#36 JIS#46 JIS#54 JIS#60 JIS#70 JIS#80 JIS#90 JIS#100 JIS#120 JIS#150 JIS#180

Typical Physical Properties of Zirconia Fused Alumina 25

01.

Characteristic

Zirconia fused alumina sand has the characteristics of compact structure, high hardness, good wear resistance, and large specific gravity, and can be used as an abrasive to grind and polish steel castings, alloy steel, carbon steel, hard bronze, and other workpieces.

02.

Mechanical Strength

Zirconia fused alumina has high mechanical strength, good thermal shock resistance, high-temperature resistance, and corrosion resistance, and is a high-quality refractory material.